Infrared Cordierite Ceramic Honeycomb Plate For Burnner
- Material: Cordierite
- Hole density:200-320 cpsi
- Hole diameter:1.12-1.42mm
- Volume:0.45-0.65g/cm3
- Product description: Cordierite infrared ceramic honeycomb plate for burnner
The infrared honeycomb ceramic plate is mainly made of cordierite material,it has a better heat storage and combustion support by increasing the surface area of the honeycomb ceramic plate from a simple planar shape into a corrugated shape called a corrugated shape, and increasing the specific surface area and the combustion working area. Heating, drying and heat preservation with an infrared burner can save energy consumption by more than 50% and reduce pollution.
Technical parameter:
| Hole type | Square hole | Round hole |
|
Material
|
Cordierite
|
Cordierite
|
|
Volume
|
0.45-0.65g/cm3
|
0.45-0.65g/cm3
|
|
Hole density
|
200-320 cpsi
|
260/280/320/520 cpsi
|
|
Wall thickness
|
- |
0.18-0.23/0.28-0.33/0.35-0.40mm
|
|
Hole length
|
- |
1.06/1.13/1.2mm
|
|
Hole diameter
|
1.12/1.25/1.42mm
|
- |
|
Hole center distance
|
1.8/2.2/2.7mm
|
1.33-1.59mm
|
|
Holefraction
|
33.5-46.5%
|
63.5-73.5%
|
|
Water absorption rate
|
>46%
|
>40%
|
|
Thermal expansion coefficient
|
2.0-2.3×10-6
|
2.0-2.5×10-6
|
|
Thermal stability
|
850℃-25℃,Not cracking in 3
times
|
1200℃-25℃,Not cracking in
repeated air cooling
|
|
Softening temperature
|
>1375℃
|
>1375℃
|
|
Surface burning temperature
|
1000℃-1200℃
|
1000℃-1200℃ |
|
Carbon monoxide release rate
|
≤80ppm
|
≤80ppm
|
|
Nitrogen oxide release rate
|
≤10ppm
|
≤10ppm
|
|
Compressive strength
(longitudinal)
|
>13.0Mpa
|
>10.0Mpa
|
|
Compressive strength (lateral)
|
>6.0Mpa
|
>3.0Mpa
|
Related Products
Categories
Latest News
Contact Us
Contact: Will Shi
Phone: +8615179912670
Tel: +8607992099918
Add: No.20, Jinfeng Rd., Xiashi industrial Area, Anyuan Dist., 337000, Pingxiang City, Jiangxi, China
Will
+8615179912670